Generales 3

COMPARACIÓN APROXIMADA ENTRE NORMAS
ACEROS MAQUINARIA

REPÚBLICA FED.
ALEMANA

BÉLGICA

FRANCIA

GRAN BRETAÑA

ITALIA

JAPÓN

SUECIA

RUSIA

ESPAÑA

U.S.A.

W.-Nr

DIN

NBN

AFNOR

B.5.

UNÍ

JIS

SS

GOST

UNE

AISI/SAE/ASTM

1.7034

37 Cr4

37 Cr 4

38 C 4

530 A 36

36 CrMn4:38 CrMn 4
KB: 38 Cr 4

SCr 435 H

 

40Ch

F.1201-38 Cr 4

5135

1.7035

41 Cr 4

41 Cr 4

42 C 4

530 M 40

41 Cr 4

SCr 440 (H)

 

40Ch

F.1202-42 Cr 4

5140

1.7045

42 Cr 4

 

42 C 4 TS

 

 

SCr 440

2245

40Ch

F.1202-42 Cr 4

5140

1.7131

16 MnCr 5

16 Mn Cr 5

I6 MC 5

527 M 17

16 MnCr 5

 

2511

18ChG

F.1516 -16 MnCr 5

5115

1.7147

20 MnCr 5

 

20 MC 5

 

20 MnCr 5

SMnC 420H

 

18ChG

F.150.D

5120

1.7176

55 Cr 3

55 Cr 3

55 C 3

527 A 60

 

SUP 9 (A)

 

50ChGA

F.1431-55 Cr 3

5155

1.7218

25 CrMo 4

25 CrMo 4

25 CD 4

1717 CDS 110

25 CrMo 4 (KB)

SCM 420: SCM 430

2225

30ChM

F.8372-AM 26CrMo4:
F.8330-AM 25CrMo4:
F.1256-30 CrMo 4-1

4130

1.7220

34 CrMo 4

34 CrMo 4

35 CD 4

708 A 37

35 CrMo 4

SCM 432: SCCrM 3:
SCM 435 H

2234

AS38ChGM:35ChML
35ChM

F.8331-AM 34 CrMo 4:
F.8231-34 CrMo 4:
F.1250-35 CrMo 4

4135:4137

1.7223

41 CrMo 4

41 CrMo 4

42 CD 4TS

708 M 40

41 CrMo 4

SCM 440

2244

40ChFA

F.8332-AM42 CrMo 4:
F.8232-42 CrMo 4:
F.1252-40 CrMo 4:

4142:4140

1.7225

42 CrMo 4

42 CrMo 4

42 CD 4

708 M 40

42 CrMo 4

SCM 440 (H)

2244

 

F.8332-AM42 CrMo 4:
F.8232-42 CrMo 4:
F.1252-40 CrMo 4:

4140

1.7228

50 CrMo 4

 

 

 

 

SCM 445 (H)

 

50ChFA

 

4150

1.7242

16 CrMo 4

18 CrMo 4

 

 

 

SCM 418

 

 

F.1550-18 CrMo 4

 

1.7262

15 CrMo 5

 

12 CD 4

 

 

SCM 415 (H)

2216

 

F.1551-12 CrMo 4

 

1.7264

20 CrMo 5

 

18 CD 4

 

 

SCM 421

 

 

F.1559-18 CrMo 4-1

 

1.7335

13 CrMo 4 4

14 CrMo 45

15 CD 3.5:15 CD 4.5

1501-620 Gr.27:31

14 CrMo 4 5

 

 

12ChM:15ChM

F-2631-14 Mo 4 5

A 182- F11 F12

1.7361

32 CrMo 12

32 CrMo 12

30 CD 12

722 M 24

32 CrMo 12

 

2240

 

F.124-A

 

1.7380

10 CrMo 9 10

 

12 CD 9.10
10 CD 9.10

1501-622 Gr 31:45

12 CrMo 9 10:
G 14 CrMo 9 10

 

2218

 

TU.H

A182F22

1.7715

14 MoV 6 3

13 MoCrV 6

 

1503-660-440

 

 

 

 

F.2621-13.MoCrV 6

 

1.8159

50CrV 4

50 CrV 4

50 CV 4

735 A 50

50 CrV 4

sup10

2230

50ChGFA

F.1430-51 CrV 4

6150

1.8507

34 CrAlMo 5

34 CrAlMo 5

30 CAD 6.12

905 M 31

34 CrAlMo 7

 

 

 

F.1741-34 CrAlMo 5

A 355 CI.D

1.8509

41 CrAlMo 7

41 CrAIMo 7

40 CAD 6.12

905 M 39

41 CrAlMo 7

 

2940

38ChMJuA

F.1740-41 CrAlMo 7

A 355 CI. A

1.8515

31 CrMo 12

31 CrMo 12

30 CD 12

722 M 24

31 CrMo 12:
30 CrMo 12

 

2240

 

F1712 – 31 ClMo 12

 

1.8523

39 CrMoV I3 9

39 CrMoV 13

 

897 M 39

36 CrMoV 12

 

 

 

 

 

1.8902

StE 420

 

E 420 RIFP

4360-55 E

Fe E 420

 

 

16G2AF

AE 420 KG

A 6 33 Gr. E

1.8905

StE460

 

E 460 RIFP

 

Fe E 460

 

 

18G2AFps

AE 460KG

A 633 Gr. E

 

 

COMPARACIÓN APROXIMADA ENTRE NORMAS
ACEROS PARA HERRAMIENTAS

REPÚBLICA FED.
ALEMANA

FRANCIA

GRAN BRETAÑA

ITALIA

JAPÓN

SUECIA

RUSIA

ESPAÑA

U.S.A.

W.-Nr

DIN

AFNOR

B.5.

UNÍ

JIS

SS

GOST

UNE

AISI/SAE/ASTM

1.1525

C 80 W I

Y1 90: Y1 80

 

C 80 KU

 

 

U8A

 

W 108

1.1545

C 105 WI

Y1 105

 

C 100 KU

 

1880

UIOA

 

W 110

1.1625

C 80 W 2

 

 

 

SKC 3 SK5:SK 6

 

U8

F .5107 C80

 

1.1645

C 105 W 2

 

 

 

SK3

 

U1O

F.5117
C 102

 

1.1663

C 125 W

Y2 I20

 

C 120 KU

SK2

 

U13

F.5123
C 120

W 112

1.1673

C 135 W

Y2 140

 

C 140 KU

SK1

 

 

 

 

1.2067

100 Cr 6

Y 100 C 6

BL 3

 

 

 

 

F .5230
100 Cr6

L 3

1.2080

X 210 Cr 12

Z200 C 12

BD 3

X 205 Cr 12 KU

SKD 1

 

Ch12

F.5212
X 210 Cr 12

D 3

1.2210

115 CrV 3

 

 

107 CrV 3 KU

 

 

 

 

L 2

1.2343

X 38 CrMoV 5 1

Z 38CDV5

BM 11

X 37CrMoV 5 1 KU

SKD 6

 

4Ch5MFS

F.5317
X 37 CrMoV 5

H 11

1.2344

X 40 CrMoV 5 1

Z 40 CDV 5

BH 13

X40 CrMoV 5 1 1 KU

SKD 61

2242

4Ch5MF1S

F.5318
X 40 CrMoV 5

H 13

1.2363

X 100 CrMoV 5 1

Z 100 CDV 5

BA2

X 100 CrMoV 5 1 KU

SKD 12

2260

 

F.5227
X 100 CrMoV 5

A 2

1.2365

X 32 CrMoV 3 3

32 DCV 28

BH 1O

30 CrMoV 12 27 KU

 

 

3Ch3M3F

F.5313
30 CrMoV 12

H 10

.2379

1X 155 Cr VMo 12 1

Z 160 CDV 12

BD2

X155 CrVMo 12 1 ku

 

 

 

 

D2

1.2419

105 WCr 6

105 WC 13

 

107 WCr 5 KU

SK 31
SKS 2: SKS 3

2140

ChWG

F.5233 105 WCr 5

 

1.2436

X 210 CrW 12

 

 

X 215 CrW 12 1 KU

 

2312

 

F .5213
X 210 CrW 12

 

1.2510

100 MnCrW 4

 

BO 1

95 MnWCr 5 KU

 

 

 

F.5220
95 MnCrW 5

O 1

1.2542

45 WCrV7

 

BS1

45 WCrV 8 KU

 

2710

 

F.5241
45 WCrSi 8

S 1

1.2550

60 WC 7

55 WC 20

 

55 WCrV 8 KU

 

 

 

 

 

 

 

COMPARACIÓN APROXIMADA ENTRE NORMAS
ACEROS PARA HERRAMIENTAS

REPÚBLICA FED.
ALEMANA

FRANCIA

GRAN BRETAÑA

ITALIA

JAPÓN

SUECIA

RUSIA

ESPAÑA

U.S.A.

W.-Nr

DIN

AFNOR

B.5.

UNÍ

JIS

SS

GOST

UNE

AISI/SAE/ASTM

1.2567

X 30 WCrV 5 3

Z 32 WCV 5

 

X 30 WCrV 5 3 KU

SKD 4

 

 

 

 

1.2581

X 30 WCrV 9 3

Z 30 WCV 9

BH21

X 30 WCrV 9 3KU

SKD 5

 

3Ch2W8F

F 5323
X 30 WCrV9

H21

1.2601

X 165 CrMoV 12

 

 

X165 CrMoW 12 KU

 

 

2310

F 5211
X 160CrMoV 12

 

1.2606

X 37 CrMoW 5 1

Z 35 CWDV 5

BH12

 

SKD 62

 

 

 

H 12

1.2713

55 NiCrMoV 6

55 NCOV 7

 

 

SKT 4

 

5ChNM

 

L 6

1.2833

100 V 1

Y1105 V

BW 2

102 V 2 KU

SKS 43

 

 

 

W210

1.2842

90MnCrV 8

90 MV 8

BO 2

90 MnVCr 8 KU

 

 

 

 

O2

1.3202

S12-1-4-5

 

BT15

 

 

 

 

F5563
12-1-5-5

T15

1.3207

S 10-4-3-10

Z 130 WKCDV 10-10-04-04-03

BT 42

HS 10-4-3-10

SKH 57

 

 

F5553
10-4-3-10

 

1.3243

S 6-5-2-5

Z 85 DKCV 06-05-05-04-02
Z 90 DKCV 06-05-05-04-02

 

HS 6-5-2-5

SKH 65

2723

R6M55K5

F5613
6-5-2-5

 

1.3246

S 7-4-2-5

Z 110 WKCDV 07-05 04 04 02

 

HS 7-4-2-5

 

 

 

F.5615
7-4-2-5

M41

1.3247

S 2-10-1-8

Z 110 DKCWV 09-08-04-02-01

BM 42

HS 2-9-1-8

 

 

 

F.5617
2-10-1-8

M42

1.3249

S 2-9-2-3

 

BM34

 

 

 

 

F.5611
2-S-2-8

M33
M34

1.3255

S18-1-2-5

Z 80 WKCV 18-05-04-01

BT4

HS 18-1-1-5

SKH 3

 

 

F.5530
18-1-1-5

T4

1.3265

S 18-1-2-10

 

BT5

HS 18-0-1-10

SKH 4A

 

 

F.5540
18-0-2-10

T5

1.3342

SC 6-5-2

Z 90 WDCV 06-05-04-02

 

HCS 9-5-3

 

 

 

 

M3

1.3343

S 6-5-2

Z 85 WDCV 06-05-04-02

BM2

HS 6-5-3

 

2722

R6M5

F.5603
6-5-2.

M2

1.3344

S 6-5-3

Z 120 WDCV 06-05-04-03
z 1330 WDCV 06-05-04-04

 

 

SKH 52: SKH 53

 

 

F.5605
6-5-3

M 3 Class 2

1.3346 

S 2-9-1

Z 85 DCWV 08-04-02-01

BM1

 

 

 

H41

 

H 41
H 1

1.3348

S 2-9-2

Z 100 DCWV 09-04-02-02

 

HS 2-9-2

 

2782

 

F.5607
2-9-2

M7

1.3355

S 18-0-1

Z 80 WCV 18-04-01

BT 1

HS 18-0-1

SKH 2

 

R18

F.5520
18-0-1

T1

 

 

COMPARACIÓN APROXIMADA ENTRE NORMAS
ACEROS INOXIDABLES Y RESISTENTES A TEMPERATURAS ALTAS

REPÚBLICA FED.
ALEMANA

FRANCIA

GRAN BRETAÑA

ITALIA

JAPÓN

SUECIA

RUSIA

ESPAÑA

U.S.A.

W.-Nr

DIN

AFNOR

B.5.

UNÍ

JIS

SS

GOST

UNE

AISI/SAE/ASTM

1.4000
1.4001

X 7 Cr 13
X 7 Cr 14

Z 6 C13
Z 3 C14

403 S 17

X 6 Cr 13

SUS 403
SUS 410 S

2301

08Ch13

F.3110 – X 6 Cr 13
F.8401 AM X 12 Cr 13

403
410 S

1.4002

Z 6 CrAI 13

Z 6 CA 13

405 S 17

X 6 CrAl 13

SUS 405

 

 

F.3111- X 6 CrAl 13

405

1.4005

X 12 Cr S 13

Z 12 CF 13

416 S 21

X 12 CrS 13

SUS 416

2380

 

F.3411 X 12 CrS 13

416

1.4006

X 10 Cr 13

Z 12 C 13

410 S 21

X 12 Cr 13
X 10 Cr 13

SUS 410

2302

12Ch 13 15
Ch 13L

F.3401 X 12 Cr 13

410

1.4008

G X 8 Cr 14

Z 12 CN 13 M

410 C 21

GX 12 Cr 13

SCS 1

 

 

 

 

1.4016

X 8 Cr 17

Z 8 C 17

430 S 15

X 8 Cr 17

SUS 430

2320

12Ch17

F.3113 X 8 Cr 17

430

1.4021

X 20 Cr 13

Z 20 C 13

420 S 37

X 20 Cr 13

SUS 420 J 1

2303

20Ch 13

F.3402 X 20 Cr 13

420

1.4024

X 15 Cr 13

 

420 S 29

 

SUS 410 J 1

 

 

 

 

1.4027

G X 20 Cr 14

Z 20 C 13 M

420 C 29

 

SCS 2

 

20Ch13L

 

 

1.4028

X 30 Cr 13

Z 30 C 13

420 S 45

X 30 Cr 13

SUS 420 J 2

2304

30Ch 13

F.3404 – X30 CR 13

 

1.4034

X46Cr 13

Z 40 C 14
Z 38 C 13 M

(420 S 45)

X 40 Cr 14

 

 

40CH13

F.3405 X 46 Cr 13

 

1.4057

X 22 CrNi 17

Z 15 CN 10.02

431 S 29

X 16 CrNi 16

SUS 481

 

 

F.3427 X16 CrNi 16

431

1.4104

X 12 CrMoS 17

Z 10 CF 17

 

X 10 CrS 17

SUS 430 F

2383

 

F.3117 X10 CrS 17

430 F

1.4113

X6CrMo17

Z 8 CD 17.01

434 S 17

X 8 CrMo 17

SUS 434

2326

 

 

434

1.4125

X 105 CrMo 17

Z 100 CD 17

 

 

SUS 440 C

 

 

 

440 C

1.4301

X 5 CrNi 18 9

Z 6 CN 18 09

304 S 15

X 5 CrNi 18 10

SUS 304

2332

08Ch18N10

F.3551 X 5 CrNi 18 11
F.3541 X 5 CrNi 18-10
F.3504 X 6 CrNi 19-10

304 304H

1.4303

X 5 CrNi 19 11

Z 8 CN 18.12

305 S 19

X8 CrNi 19 10

SUS 305

 

06Ch18N11

F.3513 X 8 CrNi 18 12

308:305

1.4305

X 12 CrNi 18 8

Z 10 CNF 18.09

303 S 21

X 10 CrNiS 18 09

SUS 303

2346

 

F.3508X10 CrNiS 18 09

303

1.4306

X 2 CrNi 18 9
G X 2 CrNi 18 9

Z 2 CN 18,10
Z3 CN 19.10 M
Z2CN18.09

304 S 12
304 C 12

X 2 CrNi 18 11
GX 2 CrNi 1910

SCS19
SUS 304 L

2352:2333

03Ch18NH

F .3503 X 2 CrNi 19 10

304 L

1.4308

G X 6 CrNi 18 9

Z6CN 18.10 M

304 C 15

 

SCS13

 

07CÍ118N9L

 

 

1.4310

X 12 CrNi 17 7

Z 12 CN 17.07
Z 12 CN18.07

 

X 12 CrNi 17 07

SUS 301

 

 

F.3517 X 12 CrNi 17 07

301

1.4311

X2 CrNiN 18 10

Z 2 10.10 Az

304 S 62

X 2 CrNi 18 11

SUS 304 LN

2371

 

 

304 LN

1.4312

G X 10 CrNi 18 8

Z 10 CN 18.9 M

302 C 25

 

SCS 12
SCS 13 A

 

10Ch18N9MLS
10Ch18N9L

 

 

 

 

COMPARACIÓN APROXIMADA ENTRE NORMAS
ACEROS INOXIDABLES Y RESISTENTES A TEMPERATURAS ALTAS

REPÚBLICA FED.
ALEMANA

FRANCIA

GRAN BRETAÑA

ITALIA

JAPÓN

SUECIA

RUSIA

ESPAÑA

U.S.A.

W.-Nr

DIN

AFNOR

B.5.

UNÍ

JIS

SS

GOST

UNE

AISI/SAE/ASTM

14313

X 5 CrNi 13 4
G5 CrNi 13 4

Z 4 CND 13.4 M

425 C 11

GX 6 CrNi 13 04

SCS 5

2385

 

 

 

1.4401

X 5 CrNiMo 18 10

Z 6 CND 17.11

316 S 16

X 5 CrNiMo 17 12

SUS 316

2347

 

F.3543 X 5 CrNiMo 17-12
F.3534 X 6 CrNiMo 17-12-03

316

1.4404

X 2 CrNiMo18 10
GX2 CrNiMo 18 10

Z 2CND 18.13
Z 2 cnd 17.12
Z 3 CND 19.10 M

316 S 11
316 S 12

x 2 CrNiMo 17 12 GX
2 CrNiMo 19 11

SUS 316 L

2348

 

F.3533 X 2 CrNiMo 17 12-03

316 L

1.4406

X2 CrNiMoN 18 12

Z 2 CND 17.12Az

316 S 61

X2 CrNÍMoN 17 12

SUS 316 LN

 

 

 

316 LN

1.4408

G X 6 CrNiMo 18 10

 

316 C 16

 

SCSI4

 

 

F.8414 AM X7 CrNiMo 20 10

 

1.4429

X2 CrNiMoN 18 13

Z 2 CND 17.13

 

X 2 CrNMoN 17 13

(SUS 316 NI)

2375

 

 

316 LN

1.4435

X 2 CrNiMo 18 12

Z 2 CND 17.13

316 S 11
316 S 12

X 2 CrNiMo 17 13

SCS16
SUS 316 L

2353

03Ch17N14M2

F.3533 X 2 CrNiMo 17 12 03

316 L

1.4436

X 5 CrNiMo 18 12

Z 6 CND 17.12

316 S 16

X5 CrNiMo 17 13

SUS 316

2343

 

F.3534 X 6 CrNiMo 1712 03

316

1.4438

X 2 CrNiMo 1816

Z 2 CND 19.15

317 S 12

X2 CrNiMo 18 16

SUS 317 L

2367

 

 

317 L

1.4449

X 5 CrNiMo 17 13

 

317 S 16

X5 CrNiMo 18 15

SUS 317

 

 

 

317

1.4460

X 8 CrNiMo 27 5

 

 

 

SUS 329 J 1
SHC 11:SCS 11

2324

 

F.3309 X 8 CrNiMo 27 05

329

1.4510

X 8 CrTl 17

Z 8 CT 17

 

X 6 CrTi 17

SUS 329 J 1
SHC 11:SCS 11

 

08Ch-17T

F.3114 X 8 CrTi 17

XM8
430 Ti

1.4511

X 8 CrNb 17

Z8 CNb 17

 

X 6 CrNb 17

SUS 430 LX

 

 

 

 

1.4512

X 5 CrTi 12

Z6CT12

409 S 19

X 6 CrTi 12

SUH409

 

 

 

409

1.4541

X 10 CrNiTi18 9

Z6 CNT 18.10

321 S 12

X 6 CrNiTi 1811

SUS 321

2337

12Ch18N10T
Ch18N10T
09Ch18N10T

F.3553 X 7 CrNiTi 18-11
F.3523 X6 CrNiTi 18-11

321

1.4542

X 5 CrNiCuNb 17 14

Z 6 CNU 17.04

 

 

SCS24
SUS 630

 

 

 

630

1.4546

X5 CrNiNb 18 l0

 

347 S 17
347 S 18

X 6 CrNiNb 18 11

 

 

 

 

348

1.4550

X 10 CrNiNb 18 9

Z 6 CNNb18.l0

347 S 17

X 6 CrNiNb 18 11 X 8 CrNiNb 18 11

SUS 347

2338

08Ch18N12B

F.3552 X 7 CrNiNb 18-11
F.3524 X 6 CrNiNb 18-11

347

1.4552

G X 5 CrNiNb 18 9

Z 6 CNNb 8.10M

347C17

 

SCS21

 

 

 

 

1.4571

 X 10 CrNiMoTi 18 10

Z 6 CNDT 17.12

320 S 31
320 S 17

X 6 CrNiMoTi 17 12

 

2350

10Ch17N13M2T

F.3535 x 6 CrNiMoTi 17-12-03

316Ti

 

 

COMPARACIÓN APROXIMADA ENTRE NORMAS
ACEROS INOXIDABLES Y RESISTENTES A TEMPERATURAS ALTAS

REPÚBLICA FED.
ALEMANA

FRANCIA

GRAN BRETAÑA

ITALIA

JAPÓN

SUECIA

RUSIA

ESPAÑA

U.S.A.

W.-Nr

DIN

AFNOR

B.5.

UNÍ

JIS

SS

GOST

UNE

AISI/SAE/ASTM

1.4573

X 10 CrNiMoTi 18 12

 

320 S 33

X 6 CrNiMoTi 17 13

 

10Ch17N13M3T
08Ch17N13M2T

10Ch17N13M3T
08Ch17N13M2T

 

316Ti

1.4580

X 10 CrNiMoNb 18 10

Z 6 CNDNb 17.12
Z 6 CNDNb 19.13

 

X 6 CrNiMoNb 17 12

 

08Ch16N13M2B

08Ch16N13M2B

 

(316 Cb)

1.4581

G X 5 CrNiMoNb 18 10

Z 4 CNDNb 18.12 M

318C 17

GX6CrNiMoNb2011

SCS 22

 

 

 

 

.4583

1X 10 CrNiMoNb 18 12

 

 

X 6 CrNiMoNb 17 13

 

 

 

 

318

1.4718

X 45 CrSi 9 3

Z 45 CS 9

401 S 45

X 45 CrSi 3

SUH 1

 

40Ch9S2

F.322 (s/Mo)

HNV3

1.4724

X 10 CrAl 13

Z 10 C 13

(403 S 17)

X 10 CrAl 12

 

 

10Ch13SJu

F.3152 X 10 CrAl 13

 

1.4731

X 40 CrSiMo 10 2

Z 40 CSO 10

 

 

SUH 3

 

40CH10S2M

 

 

1.4742

X 10 CrAl 18

Z 10 CAS 18

(430 S 15)

(X 8 Cr 17)

SUS 430
SUH 21

 

 

F.3153 X 10 CrAl 18

430

1.4747

X 80 CrNiSi 20

Z 80 CSN 20.02

443 S 65

X 80 CrSiNi 20

SUH 4

 

 

F.320 B

HNV6

1.4762

X 10 CrAl 24

Z 10 CAS 24

 

X 16 Cr 26

 

 

 

F.3154 X 10 CrAl 24

 

1.4828

X 15 CrNiSi 20 12

Z 15 CNS 20.12

(309 S 24)

 

SUH 309

 

20Ch20N14S2

F.3312 X 15 CrNiSi 20 12

309

1.4833

X7 CrNi 23 14

Z 15 CN 24.13

 

X 6 CrNi 23 14

SUS 309 S

 

 

 

309 S

1.4837

G X 40 CrNiSi 25 12

 

209 C 30

GX35 CrNi 25 12

SCH 17
SCS 17

 

40Ch24N12SL

 

 

1.4841

X15 CrNiSi 25 20

Z 12 CNS 25.20

 

X 16 CrNiSi 25 20

SUH 310

 

20Ch25N20S2

F.3310 X 15 CrNiSi 25 20

314
310

1.4845

X 12 CrNi 25 21

Z12 CN 25.20

310 S 24

(X 6 CrNi 25 20)

SUN 310
SUS 310 S

2361

 

F.331

310 S

1.4848

G X 40 CrNiSi 25 20

 

310 C 40

GX 40 CrNi 26 20

SCH21:SCH22

 

 

F.8452 AM X 40 CrNi 25 20

 

1.4864

X 12 NiCrSi 36 16

Z 12 NCS 37.18
Z 12 NCS 35.16
Z 12 NC 37.18

 

 

SUH 330

 

 

F.3313 X 12
CrNiSi 36 16

330

1.4865

G X 40 NiCrSi 38 18

 

330 C 40

GX 50 NiCr 39 19

SCH 15: SCH 16

 

 

 

 

1.4871

X 53CrMnNiN 21 9

Z52 CMN 21.09

349 S 54

X 53 CrMnNiN 219

SUH 35:SUH 36

 

55Ch20G9AN4
5Ch20N4AG9

 

EV8

1.4873

X 45 CrNiW 18 9

Z 35 CNWS 14.14

(331 S 40)

X 45 CrNiW 18 9

SUH 31

 

 

 

 

1.4876

X 10 NiCrAITi 33 20

Z 8 NC 32 21

NA 15 (H)

 

NCF 800

 

 

F.3545 X 9 NiCr 33 21
F.3314 X 10 NiCrAITi 32 20

B 163

1.4878

X 12 CrNiTi 18 9

Z 6 CNT 18 12 (B)

(321 S 12)
321 S 20

(X 6 CrNiTi 18.11)

SUS 321

2337

12Ch18N10T

F.3523 X 6 CrNiTi 18 11

321